Exaton Ni71 is a covered electrode with basic coating and a normal metal recovery for welding of NiCrFe alloys such as Alloy 600, 800 and 800H. 9%Ni steels as well as nickel-alloyed steels for cryogenic temperature use. It is also used for dissimilar joints such as stainless steel and NiCu alloys to carbon steel and nickel alloys. Exaton Ni71 is characterised by little spatter and very good slag removal. Typical applications are found in constructions to be used at lower temperatures e.g. 3.5%, 5% and 9% Ni steels are used as well as austenitic Cr-Ni stainless steel, especially if the weld metal is to be thermoformed or stress relieved. The alloy can be used in air up to 1200°C (2150°F), in sulphur dioxide atmospheres up to 800°C (1470°F) and in ammonia at the highest process temperature. This alloy is used for surfacing or joining where there are strict requirements on stress corrosion resistance and for high temperature service. The microstructure is fully austenitic.
Типичные свойства образца с V-образным надрезом по Шарпи
Механические свойства при растяжении
| Защитный газ |
Предел прочности при растяжении |
Предел текучести |
Продолжительность испытаний |
Состояние |
Температура испытания |
Удлинение |
| AWS |
635 MPa (92 ksi) |
400 MPa (58 ksi) |
16 hr |
PWHT |
610 degC (1130 degF) |
50 % |
Данные наплавки
| Ток |
Производительность наплавки при токе 90% от максимального |
Диаметр |
| 50-70 A |
0.0 kg/h (0.0 lb/h) |
2.5 x 300.0 mm (0.098 x 11.8 in.) |
| 65-105 A |
0.0 kg/h (0.0 lb/h) |
3.2 x 350.0 mm (1/8 x 13.8 in.) |
| 75-150 A |
0.0 kg/h (0.0 lb/h) |
4.0 x 350.0 mm (5/32 x 13.8 in.) |
| 120-170 A |
0.0 kg/h (0.0 lb/h) |
5.0 x 350.0 mm (0.197 x 13.8 in.) |
Классификации
| Классификации |
SFA/AWS A5.11 : ENiCrFe-3
EN ISO 14172 : E Ni 6182 (NiCr15Fe6Mn) |
Одобрения
| Одобрения на материалы выдаются с привязкой к заводу изготовителю. Подробную информацию можно получить в представительствах ESAB. |
Характеристики расходного материала
| Тип сплава |
Ni based Cr alloy |
| Тип покрытия |
Basic |
| Сварочный ток |
DC+ |
Хим. состав наплавленного металла
| Хим. состав наплавленного металла |
| Al |
C |
Cr |
Cu |
Fe |
Mn |
Mo |
Nb |
Ni |
P |
S |
Si |
Ti |
Ti+Nb |
| 0.009 % |
<=0.03 % |
16 % |
0 % |
<=10 % |
5.7 % |
0.005 % |
2.2 % |
67 % |
<=0.015 % |
<=0.010 % |
0.3 % |
0.08 % |
<0.50 % |