Exaton Ni41Cu welding wire is suitable for overlay welding when a deposit with chemistry corresponding to UNS N08825 is required. The weld deposit is a nickel-iron-chromium-molybdenum-copper alloy suitable for use in extremely corrosive environments. Exaton Ni41Cu has very good resistance to stress corrosion cracking (SCC) in chloride containing environments and is particularly suited for use in reducing environments such as those containing sulphuric and phosphoric acids. Exaton Ni41Cu is used for corrosion resistant alloy surfacing of components in the chemical, pollution control, oil & gas and petrochemical industries and often in connection with sour gas service. Typical components are tanks, heat exchangers, evaporators, transport pipes and scrubbers etc. It is used for MIG/MAG welding.
Механические свойства при растяжении
| Предел прочности при растяжении |
Предел текучести |
Состояние |
| 550 MPa (80 ksi) |
340 MPa (49 ksi) |
После сварки |
Данные наплавки
| Current |
Voltage |
Диаметр проволоки |
Wire Feed Speed |
| |
| 60-220 A |
15-28 V |
1.0 mm (0.040 in.) |
4.0-12.0 m/min (157-472 in./min) |
| 150-260 A |
24-29 V |
1.2 mm (0.047 in.) |
3.0-10.0 m/min (118-394 in./min) |
| 230-350 A |
25-30 V |
1.6 mm (1/16 in.) |
3.0-5.0 m/min (118-197 in./min) |
Классификации
| Wire Electrode |
SFA/AWS A5.14 : ERNiFeCr-1
EN ISO 18274 : S Ni 8065 (NiFe30Cr21Mo3) |
Хим. состав наплавленного металла
| Хим. состав проволоки |
| C |
Cr |
Cu |
Fe |
Mn |
Mo |
Ni |
P |
S |
Si |
| <=0.025 % |
23 % |
2.3 % |
>=22.0 % |
1 % |
3 % |
>=42.0 % |
<=0.025 % |
<=0.010 % |
<=0.3 % |